Quick Details
Grade: S32101/1.4162/2101 LDX
Standard: AISI, ASTM, DIN, EN, GB, JIS
Thickness: 0.3MM--12.0
Width: 10MM--1500MM
Length: COIL
Place of Origin: China (Mainland)
Model Number: Duplex stainless steel
Technique: COLD ROLLED/HOT ROLLED
Application: Bridges, kitchenware,decoration,Saltwater handling,
Certification: SGS BV ISO
Surface: 2B BA No.4 with PE
Note: We can also do other materials
Special Use: High-strength Steel Plate
Sample: Free
Size can process: as your required
State: plate/rod/pipe
Best service: After sales service
small order: Do best
Delivery: short
Name: Duplex stainless steel
Packaging & Delivery
Packaging Details:Delivery Detail:
wooden box for Duplex stainless steel |
5 DAYS Or according your quantity |
Product Description
Duplex Steel S32101/1.4162/2101 LDX Duplex stainless steel coil/strips
Introduction
Stainless steel grade Duplex 2101 LDX is a low-alloyed, general-purpose duplex. This steel possesses high tensile strength as well as high fatigue strength. Its high mechanical strength is same as other duplex grades, and its good corrosion resistance is equal to most standard stainless steel grades. All these properties are utilized to design products with strength, low maintenance, durability and long-term cost efficiency.
The following datasheet provides an overview of stainless steel grade Duplex 2101 LDX.
Chemical Composition
The chemical composition of stainless steel grade Duplex 2101 LDX is outlined in the following table.
ElementContent (%)
Iron, Fe |
71.45 |
Chromium, Cr |
21.5 |
Manganese, Mn |
5 |
Nickel, Ni |
1.5 |
Molybdenum, Mo |
0.3 |
Nitrogen, N |
0.220 |
Carbon, C |
0.03 |
Mechanical Properties
The mechanical properties of stainless steel grade Duplex 2101 LDX are displayed in the following table.
PropertiesMetricImperial
Tensile strength (annealed) |
696 MPa |
101000 psi |
Yield strength (@strain 0.200 %) |
450 MPa |
65300 psi |
Modulus of elasticity |
200 GPa |
29000 ksi |
Shear modulus |
77 GPa |
11200 ksi |
Poisson's ratio |
0.3 |
0.3 |
Elongation at break (In 2", 50% cold worked) |
38% |
38%
|